Apparatus for measuring reflectivity

ABSTRACT

An apparatus for measuring the reflectivity of magnetooptic materials where the complex reflection coefficients of absorbing anisotropic media are determined. Amorphous rare-earth transition metal alloys exhibiting polar Kerr effect are analyzed for use as storage media in erasable optical storage systems.

GOVERNMENT SUPPORT

This work was supported by the United States Government under National Science Foundation Grant No. ECS-8307928.

BACKGROUND OF THE INVENTION

Amorphous rare earth-transition metal alloys (RE-TM) can possess strong perpendicular anisotropy and exhibit polar Kerr effect when prepared as thin films with appropriate compositions. This property makes RE-TM films good candidates for storage media in erasable optical storage system using thermomagnetic writing and magnetooptical readout. See P. Chaudhari, N. J. Cuomo, and R. J. Gambino, "Amorphous Metallic films for Magneto-Optic Applications," Appl. Phys. Lett. 22, 337 (1973). R. P. Freese, R. N. Gardner, T. A. Rinehart, D. W. Siitari, and L. H. Johnson, "An Environmentally Stable, High Performance, High Data Rate Magneto-Optic Media," Proc. Soc. Photo-Opt. Instrum. Eng. 529,6 (1985).

Reflection of light falling at oblique incidence on the boundary between two media of different refractive indices is usually described by two Fresnel amplitude reflection coefficients r^(p) (for incident p-polarized light) and r^(s) (for incident s-polarization). These are real numbers for nonabsorbing isotropic media. For absorbing media, there is both a magnitude and phase change in the reflected light, so that the reflection coefficients are complex. G. A. N. Connell and D. S. Bloomberg, Mott Festschrift, Plenum, New York (1985). RE-TM magnetooptical media are both absorbing and anisotropic, so their r^(p) and r^(s) are complex; in addition, they possess a third complex reflection coefficient r that describes optical activity in terms of the coupling of incident p- or s- polarized light into the orthogonal polarized components of the light after reflection.

A number of traditional ellipsometric methods have been used to partially characterize optical properties of film. J. Bennett, H. Bennett, "Polarization," in Handbook of Optics (McGraw-Hill, New York; 1978), and R. M. A. Azzam and N. M. Bashara Ellipsometry and Polarized Light (North-Holland, New York, 1977). Ellipsometry measured the reflection of polarized light striking a material at oblique incidence by nulling the reflected signal with an analyzer. These measurements described reflecting properties in terms of the relative phase change Δ=φ^(p) -φ^(s), and the relative amplitude attenuation, tan γ=|γp|/|γs|, that are introduced by reflection from the materials. From these quantities other properties, most often surface film thickness and optical constants can be determined. Recent attempts to extend ellipsometry have used Δ and tan γ to obtain the off-diagonal elements of the dielectric tensor. See G. J. Sprokel, "Reflectivity, Rotation, and Ellipticity of Magnetooptic Film Structures." Appl. Opt. 23, 3983 (1984) and G. J. Sprokel, "Photoelastic Modulated Ellipsometry on Magnetooptic Multilayer Films," Appl. Opt. 25, 4017 (1986).

U.S. Pat. No. 3,155,944 discloses use of polarized light to read a magnetically recorded thin film. Polarized light reflected from the film and rotated by the Kerr effect is passed through an analyzer which is rotated for near extinction of the reflected light when the film is magnetized in one stable state. With the analyzer held fixed in this position, when the remanent state of the film is switched by applying a suitable field, the plane of polarization of the reflected light will be rotated resulting in a substantial increase in light intensity.

SUMMARY OF THE INVENTION

The present invention utilizes a polarized light source to illuminate a magnetooptic material so as to measure its reflective characteristics. Two detectors are mounted so as to measure the orthogonal components of the electric field intensity of the reflected polarized light. One measures the parallel component of the signal, and the other the perpendicular component.

In a preferred embodiment, the magnetooptic material is covered by a transparent protective layer to avoid any degradation of the material's surface. Due to reflection and refraction of light by the protective layer an additional lens is interposed between the layer and the light source. One embodiment utilizes a hemispherical lens having an index of refraction matching that of the protective layer. Light incident from various angles upon the magnetooptic material and its protective layer always enters the lens at a right angle. A film is placed between the lens and layer having essentially the same index of refraction as both the lens and layer so that light transmitted through the lens, the film, and the layer is not refracted or reflected prior to reaching the magnetooptic surface. Any losses due to the optics of the system can be calculated by removing the sample to allow total internal reflection by the lens. The measured signals can then be normalized by this totally reflected light.

A preferred embodiment utilizes a pulsed electromagnet to reverse the direction of magnetization of the material. This permits sign reversal of the reflection coefficient r.sub.⊥, while leaving other parameters intact.

The apparatus permits the calculation of the complex reflection coefficients of light absorbing, anisotropic and magnetooptic media. These values can be determined as a function of the angle of incidence of the polarized light on the magnetooptic material. The orientation of polarization of both the incident light and the reflected light can be adjusted.

an adjustable phase delay can be introduced between the reflected parallel and perpendicular polarization components. The phase delay is determined so as to create independent observations of the magnitudes and phases of the complex reflection coefficient.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic illustration of the apparatus for measuring reflectivity.

FIG. 2 is a cross-sectional view of the configuration of the magnetooptic material, layer, film, and lens.

FIGS. 3(a), 3(b) and 3(c) graphically depict theoretical values for the reflection coefficients of Tb₂₈ Fe₇₂.

FIGS. 4(a), 4(b) and 4(c) are graphical comparisons of theoretical and experimental values of reflection coefficients and the indicated expressions for Tb₂₈ Fe₇₂.

FIGS. 5(a), 5(b) and 5(c) are graphical comparisons of theoretical and averaged experimental values for TbFeAr.

DETAILED DESCRIPTION OF THE INVENTION

Apparatus for measuring reflectivity is illustrated in FIG. 1. A linearly polarized HeNe laser is used as a light source 10. The beam is incident on a polarizing beam splitter 11, which splits the beam into p- and s-polarized components. One component proceeds to detector 14, which is used to measure variations of the light source 10 and to normalize the output to account for these variations. The detector 14 may be rotatably attached to the beam splitter 11. Before the beam splitter 11 the laser signal is linearly polarized at an angle of 45° to the plane of the figure. The polarization vector may be rotated by rotating the beam splitter 11. The axis of the beam splitter 11 has angle β with the plane of reference, and thus the polarization vector that is incident on the sample has angle β. Lens 13 is a long focal length lens that focuses the beam on the sample through hemispherical lens 16.

The sample 17 is assumed to have a transparent overcoat layer over an optically thick film of magnetooptic material. Lens 16 allows the beam to strike the magnetic film directly at all angles of incident without being bent by the glass overcoating layer. It also reduces reflection of the incident beam at the air-overcoat boundary and trapping by internal reflection of the reflected beam as it leaves the overcoating layer. This is because the beam always enters and leaves lens 16 normally (the overcoating is negligible compared with lens 16 dimensions) and because lens 16, the index matching oil, and overcoating have the same index of refraction n.

An electromagnet 18 is used to reverse the direction of polarization of the magnetooptic material of sample 17. A pulsed electromagnet 18 can produce a field of up to 7 kOe perpendicular to the sample, and its position is such that the illuminated area of the sample always receives the strongest field. The magnet 18, sample 17, and hemispherical lens 16 are all mounted on a rotatable base 19, which pivots around an axis perpendicular to the plane in FIG. 1. The axis passes through the plane of the sample and the center of the hemispherical lens. In a preferred embodiment, the angle of incidence, θ, as measured from the normal 12 from sample 17, can be varied from a minimum of 15° to a maiximum of 88°.

The reflected beam goes through a 1/4 wave plate, 20, which, as will be shown below, will help identify the phase difference between the reflected components of polarization. The fast axis of the 1/4 wave plate 20 has angle ρ with the reference plane.

In a preferred embodiment, the beam splitter 21 and detectors 22 and 23 may be rotated by an angle η. Beam splitter 21 splits the reflected beam into two components and directs these two components into the detector 22 and 23 respectively. Alternatively, a 1/2 wave plate rotates the polarization with respect to the polarizing beam splitter whose transmission axis is parallel to the plane of reference. The angle of the fast axis of the 1/2 wave plate would then be noted by η/2. The two photodetectors 22 and 23 are identical, and their conversion factor, defined as the ratio of the output voltage to the input light intensity is α. We will denote the individual detector outputs by S₁ and S₂. Means for adding these two signals 25 is shown in FIG. 1 with the sum designated by Σ. The difference between the two signals appears at the output of the electronic differential amplifier 24, and is designated by Δ S.

FIG. 2 shows a cross section of a typical configuration of the sample 17 with the lens 16. Magnetooptic material 31 is deposited on a quartz substrate 30. A transparent protective layer 32 is then deposited onto the material 31. Hemispheric lens 16 is then placed on top of the layer 32 with a thin film matching oil 33 interposed between them. The refractive index of the film 33 matches the refractive indices of the hemispherical lens 16 and the protective layer 32. This is to insure that light being transmitted through the lens, film and layer is not refracted or reflected at any of these interfaces.

To normalize the measurement results, we must know the effective light amplitude that goes through the system. This can be measured by removing the sample and allowing the light to undergo total internal reflection at the back surface of the hemispherical lens. The angle of incidence, θ, must be larger than the critical angle (approximately 42°), but the orientation of the phase plates is arbitrary. If the effective light amplitude is denoted A the sum of the signals S₁ and S₂ will be given by σ=S₁ +S₂ =1/2(α) A². In the following discussion, we will assume that the results are normalized by σ.

The experimental results obtained from the above apparatus may be compared with a theoretical characterization. The dielectric tensor for magnetooptical media of interest can be written as ##EQU1## Where a coordinate system is chosen so that the plane of the film is x-y, and the magnetization direction z. The films are amorphous and isotropic in the x-y plane. Thus e_(x) =e_(y). Since the films are grown in the z-direction, there may be some kind of growth-induced anisotropy in this direction, such as columnar structure. We, therefore, allow e_(z) to be different from e_(x) and e_(y).

Let a plane monochromatic wave propagate in this medium along the unit vector S=(S_(x), S_(y), S_(z)). From symmetry, one can set S_(y) =0 without loss of generality; thus S_(x) ² +S_(z) ² =1. In general, the electromagnetic quantities E, D, H, and B have the following form:

    V(r,t)=V.sub.0 exp(i[(2πn/λ.sub.0)S·r-wt])(2)

r is the position vector, ω=2πf is the frequency of the electromagnetic disturbance, λ₀ =c/f is the vacuum wavelength, and n is the refractive index of the medium to be determined below. From Maxwell's equations ##EQU2## where B=μH. At the optical frequencies μ=1, and we can write ##EQU3##

Replacing for E and D from Eq. (2) we arrive at

    n.sup.2 [E.sub.0 -(S·E.sub.0)S]=D.sub.0           (5)

Now D₀ =eE₀, and, therefore, ##EQU4##

Equation (6) will have a nontrivial solution if and only if the determinant of the matrix is equal to zero. This yields the following fourth-order equation in n: ##EQU5##

In general, there will be two solutions, n₁ and n₂, for the medium specified by the dielectric matrix of Eq. (1). Once n is replaced in Eq. (6) the E vector will be determined within a multiplicative constant. The magnetic field vector H can also be obtained in terms of E. Replacing for E and B in Eq. (3a) from Eq. (2) and setting μ=1 we obtain

    H.sub.0 =n(S×E.sub.0)                                (8)

Let us now consider the interface of our magnetooptic medium with a homogeneous medium of refractive index n₀. The interface is the plane z=0, and the beam is incident from the isotropic medium at an angle θ, as shown in FIG. 2. The continuity of the tangential components of E and H at the interface requires that the reflected beam and both refracted components remain in the x-y plane. Moreover, the reflected beam will have the same angle θ with the normal as the incident beam and (Snell's law);

    n.sub.0 sin θ=n.sub.1 S.sub.x1 =n.sub.2 S.sub.x2     (9)

Replacing nS_(x) with n₀ sin θ in Equation (7) and solving for n yield ##EQU6##

From this equation we can obtain the refractive indicies, n₁ and n₂, for the two refracted beams in terms of the dielectric tensor elements and the angle of incidence θ. Once n₁ and n₂ are determined, we resolve the incident E field into its parallel and perpendicular components E_(p).sup.(i) and E_(s).sup.(i), respectively. The continuity of E_(x), E_(y), H_(x), and H_(y) at the interface gives rise to four equations in the four unknowns E_(p).sup.(r), E_(s).sup.(r), E.sup.(t1), and E.sup.(t2). E.sup.(t1), and E.sup.(t2) are the magnitudes of the two E field vectors in the magnetooptical medium, while E_(p).sup.(r) and E_(s).sup.(r) refer to the parallel and perpendicular components of the reflected beam, respectively. To express the solutions in compact form, let us define the following parameters: ##EQU7##

Using Eqs. (10) and (11) in Eqs. (13) and (15) it is possible to show that

    r.sub.⊥.sup.(p) =-r.sub.⊥.sup.(s)                (16)

which is intuitively reasonable given the physical nature of the magnetooptical interaction. Also notice that when the magnetization is switched the sign of e_(xy) is reversed. This results in a sign reversal for r.sub.⊥ but leaves other parameters intact.

FIG. 3 shows the complex reflectivities r.sup.(p), r.sup.(s), and r for a typical magnetooptical medium. The dielectric tensor elements are e_(x) =e_(z) =-2.6+i(20.0), e_(xy) =-0.04+i(0.33), and the medium of incidence is glass (n₀ =1.5). Note that in FIG. 3(c), the magnitude and phase of r.sub.⊥ remain constant until nearly 60°. In many magnetooptical readout systems, high numerical aperture lenses are used, and incident rays far from the center of the lens can strike the medium at angles as high as 40 or 50°. FIG. 3(c) shows that the reflectivity r.sub.⊥, which determines the strength of the signal, is nearly constant for all the rays through such a lens.

When the sample is placed in the system the signals, S₁ and S₂, will in general depend on r.sup.(p), r.sup.(s), and r.sub.⊥ as well as on β, ρ, and η.

For simplicity of notation let us define ##EQU8##

Then, after some straightforward but tedious calculations, we will obtain ##EQU9##

By selecting certain values for the angles βand ρ the significance of this expression can be illustrated. Specifically, the reflection coefficient r_(p), r_(s), and r.sub.⊥, can be determined from the output signals S₁ and S₂. Assuming a λ/2 plate is used to rotate polarization consider the following experiments:

Experiment 1: Set β=0. Then

    σ/σ.sub.o =r.sub.p.sup.2 +r.sub.⊥.sup.2 ≅r.sub.p.sup.2                                  (19)

Next set β=45°. Then

    σ/σ.sub.o =r.sub.s.sup.2 +r.sub.⊥.sup.2 ≅r.sub.s.sup.2                                  (20)

Finally, set β=22.5°, ρ=0, and η=22.5°. Then

    ΔS/σ.sub.o =r.sub.p r.sub.s (sin(φ.sub.p -φ.sub.s)-r.sub.p r.sub.⊥ sin(φ.sub.p -φ.sub.⊥)-r.sub.s r.sub.⊥ sin(φ.sub.s -φ.sub.⊥)(21)

    ≈r.sub.p r.sub.s sin(φ.sub.p -φ.sub.s),

from which the phase difference between r.sup.(p) and r.sup.(s) can be obtained. The same experiment can be performed without the λ/4 plate, in which case the sine in Eq. (21) will be replaced by cosine. Another possibility is to let β=22.5° and ρ=45°. In this case Eq. (18) becomes

    -ΔS/σ.sub.0 =r.sub.⊥.sup.2 sin 4η+r.sub.p r.sub.s sin(φ.sub.p -φ.sub.s 4η)-r.sub.p r.sub.⊥ sin(φ.sub.p -φ.sub.⊥ -4η)-r.sub.s r.sub.⊥ sin(φ.sub.s -φ⊥+4η)                                      (22)

    ≈r.sub.p r.sub.s sin(φ.sub.p -φ.sub.s -4η).

η can now be adjusted for maximum or minimum signal. It can also be set to 22.5° for the same result as one would obtain without the λ/4 plate.

Experiment 2: Set β+0° and ρ=45°. Then

    ΔS/σ.sub.0 =2r.sub.p r.sub.⊥ sin(φ.sub.p-φ.sub.⊥ -4η).                (23)

Since this is a small signal, its direct measurement is subject to various errors in the system. Fortunately, it is possible to reverse the sign of r.sub.⊥ by switching the magnet and measure the difference in ΔS. This would yield ##EQU10##

By measuring δ/σ₀ at η=0° and η=22.5°, we obtain both the amplitude product r_(p) r.sub.⊥ and the phase difference φ_(p) -φ.sub.⊥.

Experiment 3: Similar to Experiment 2 but with the incident polarization being s instead of p. Thus β=45°, ρ=45°, and ##EQU11##

which is identical to Eq. (24) for s-polarized incident light. The importance of magnetization reversal is clear from these two experiments as the measurement of r.sub.⊥ is routine, given appropriate choices for the angles β and ρ.

EXAMPLE 1

The results of reflectivity measurements on a Tb₂₈ Fe₇₂ sample are presented in FIG. 4. The sample was sputter deposited on a quartz substrate and in situ overcoated with a 300 Å layer of silicon dioxide. The thickness of the TbFe layer is approximately 1000 Å, which, for all practical purposes is optically thick.

The three sets of data correspond to the three experiments discussed above. The solid curves are theoretical results obtained for e_(x) =e_(z) =-2.6+i(20), which is the same value obtained by Connell et al. See G. A. N. Connell and D. S. Bloomberg "Amorphous Rare Earth Transition Metal Alloys," Mott Festschrift, Plenum, New York, 1985. Connell's results are for TbFe samples deposited under similar conditions. Connell's measurement, however, were performed at normal incidence, and did not provide information on the value of e_(z). The good match between theory and experiment here suggest that the assumption e_(x) =e_(z) for these samples is not a bad assumption, although structural anisotropy in the perpendicular direction is known to occur in samples deposited under other conditions (such as high argon pressure). Also, the presence of cobalt in an alloy is usually accompanied by columnar growth in the perpendicular direction. In such situations, our method is capable of providing information about the existence and strength of the structural anisotropy.

FIG. 4b shows the results of experiment 2. The data represent reflection coefficients plotted versus the angle of incidence, and the solid curves are obtained from theoretical calculations using e_(xy) =-0.04+i(0.33). This is Connell's value for e_(xy).

FIG. 4c corresponds to the third experiment, and the data shown here are the indicated functions plotted versus θ. The values e_(x), e_(z), and e_(xy) are the same as above. The general behavior and numerical value of the results are in good agreement. Discrepencies at 85° and above are attributed to the spreading of the incident beam on the film surface at large angles of incidence. The beam spot becomes larger than the constant field region of the magnet, and undergoes distortion on leaving the hemispherical lens because some rays are not reflected from the center of curvature.

EXAMPLE 2

FIG. 5 compares theoretically estimated curves with averaged data from four experiments. The designated functions are plotted versus the angle of incidence θ. One standard deviation ranges over the four experiments are shown as error bars at each angle. The functions f₁, f₂, f₃, f₄, f₅, f₆ and f₇ are defined in Table 1:

                  TABLE I                                                          ______________________________________                                         f.sub.1          r.sub.p.sbsb.2.sup.2                                          f.sub.2          r.sub.s                                                       f.sub.3          r.sub.p r.sub.s cos(φ.sub.p -φ.sub.s)                 f.sub.4          r.sub.p r.sub.⊥ sin(φ.sub.p -φ.sub.⊥)       f.sub.5          r.sub.p r.sub.⊥ cos(φ.sub.p -φ.sub.⊥)       f.sub.6          r.sub.s r.sub.⊥ sin(φ.sub.s -φ.sub.⊥)       f.sub.7          r.sub.s r.sub.⊥ cos(φ.sub.s -φ.sub.⊥)       ______________________________________                                    

The sample with composition (Tb₁₇.9 Fe₈₂.1) AR₁₁.8 had a TbFe layer of 2000Å with 500Å of Al₂ 0₃ as overcoat. Observations were taken over a period of a month, starting about two months after the sample was deposited. Each column of Table II shows estimates from one experiment, while the last column represents estimates based on the averages of the observations, in an attempt to eliminate the effects of random experimental variability. The variability in estimates is due to variations in the data, especially at higher angles of incidence. Variability across the four experiments of ±5% was common at angles above 70° for almost every function measured.

                  TABLE II                                                         ______________________________________                                         ESTIMATE   1       2       3     4     AVG Data                                ______________________________________                                         Re(e.sub.x)                                                                               -2.91   -2.55   -3.09 -2.82 -2.91                                   Im(e.sub.x)                                                                               9.49    12.50   9.11  9.76  10.10                                   Re(e.sub.xy)                                                                              -0.067  -0.065  -0.064                                                                               -0.066                                                                               -0.068                                  Im(e.sub.xy)                                                                              0.104   0.156   0.152 0.113 0.115                                   Fig. Merit × 10.sup.3                                                               6.52    6.78    6.58  6.72  6.59                                    ______________________________________                                    

The figure of merit is given by the right-hand side of the expression: ##EQU12##

This expression provides an upper bound on the ratio of useful magneto-optical signal to incident laser power available from the medium. Thus, r.sub.⊥ is a measure of the usefulness of materials for erasable memory systems.

The estimates from the averaged data for e_(x) (-2.91+i10.1) and e_(xy) (-0.068+i0.115) are comparable to published values for TbFe films of similar composition. The figure of merit for the sample is 6.59×10⁻³. The estimates were used to recreate the observations in FIG. 5. Discrete symbols show the averaged observations for each function and the solid lines are the predicted reflectivity curves using the estimated dielectric tensor values.

The estimated dielectric tensor elements were obtained through the use of the multivariate gradient algorithm of Levenberg-Marquardt. See K. M. Brown and J. E. Dennis, Numerische Mathematick 18:289 (1972).

While the invention has been particularly shown and described with reference to preferred embodiment thereof, it will be understood by those skilled in the art that various changes in form and details may be made without departing from the spirit and scope of the invention as defined in the appended claims. 

We claim:
 1. Apparatus for measuring reflectivity comprising:a polarized light source; a first rotatable device to rotate a direction of polarization of polarized light from the source to any of a plurality of selectable angles; a magnettooptic material illuminated by and reflecting light from the source; a second device positionable in any of a plurality of selectable positions to alter the phase of the light reflected by the material; a third device for rotating the direction of polarization of the reflected light; first and second detectors to simultaneously measure the intensity of the electric field of light reflected by said material in two orthogonal planes; and determining means for determining reflection coefficients of the magnetooptic material with the measured intensities.
 2. Apparatus for measureing reflectivity as defined in claim 1 wherein said material is covered by a transparent protective layer.
 3. Apparatus for measuring reflectivity as defined in claim 2 wherein a lens is placed on the protective layer such that light normally incident upon said lens is essentially not refracted or reflected by the lens or the layer during transmission through the lens and the layer, and after reflection by the material.
 4. Apparatus for measuring reflectivity as defined in claim 3 wherein the lens and layer are interfaced by a film having a refractive index essentially the same as the refractive index of both the lens and the layer.
 5. Apparatus for measuring reflectivity as defined in claim 4 wherein said film is comprised of silicon dioxide.
 6. Apparatus for measuring reflectivity as defined in claim 4 wherein said film is comprised of Al₂ O₃.
 7. Apparatus for measuring reflectivity as defined in claim 1 further comprising means for adjusting the angle of incidence of the polarized light on said material.
 8. Apparatus for measuring reflectivity as defined in claim 1 wherein the magnetooptic material is light absorbing and anisotropic.
 9. Apparatus for measuring reflectivity as defined in claim 1 wherein said magnetooptic material is a rare earth-transition metal alloy.
 10. Apparatus for measuring reflectivity as defined in claim 9 wherein said material is an amorphous TbFe alloy.
 11. Apparatus for measuring reflectivity as defined in claim 1 further comprising means for using said measured amplitudes in determining the reflection coefficeints r_(p), r_(s) and r.sub.⊥ of the material.
 12. Apparatus for measuring reflectivity as defined in claim 11 wherein said coefficients are comprised of magnitude and phase components.
 13. Apparatus for measuring reflectivity as defined in claim 1 further comprising:reversing means for reversing the direction of magnetization of the material to measure a coupling of components of polarized light from the source; and a detector to measure the intensity of the electric field of light reflected by said material.
 14. Apparatus for measuring reflectivity as defined in claim 13 wherein said reversing means is comprised of an electromagnet.
 15. Apparatus for measuring reflectivity as defined in claim 14, wherein said electromagnet is pulsed.
 16. Apparatus for measuring reflectivity as defined in claim 13 wherein said reversing means is used to reverse the sign of the ratio of the intensity of one incident electric field polarization component to the intensity of the orthogonal electric field component after reflection. 